3M™ Double Coated Tape 9816M

3M ID 7000124387UPC 00051115322211
  • Double-coated
  • Aggressive, high-tack
  • Offers good heat resistance
  • White polyester film carrier with rubber adhesive on a kraft liner
 More...
View all details
Specifications
Applications
Gasket Assembly, Mounting & Trim Attachment, Small Joint Assembly
Back Side Adhesive Thickness (Imperial)
1.5 mil
Back Side Adhesive Thickness (Metric)
0.04 mm
Back Side Adhesive Type
Miscellaneous 900
Brand
3M™
Carrier Material
Polyester Film
Carrier Thickness
0.5 mil
Carrier Thickness (Metric)
0.013 mm
Face Side Adhesive Thickness (Imperial)
1.5 mil
Face Side Adhesive Thickness (Metric)
0.04 mm
Indoor/Outdoor
Both
Industries
Appliance, Automotive, Electronics, General Industrial, Medical, Specialty Vehicle, Transportation
Maximum Operating Temperature (Celsius)
49 °C
Maximum Operating Temperature (Fahrenheit)
120 °F
Minimum Operating Temperature (Fahrenheit)
-40 °F
Position
Best
Primary Liner
74# Kraft Liner
Product Colour
White
Product Form
Roll
Set Time
<10 Second
Substrate
Foam, Glass, High Surface Energy, (400-1100 Dynes/cm), LSE Plastic, Metal, Rubber (Except EPDM), Smooth
Substrate 2
Foam, Glass, High Surface Energy, (400-1100 Dynes/cm), LSE Plastic, Metal, Rubber (Except EPDM), Smooth
Total Tape Thickness without Liner (Imperial)
3.5 mil
Total Tape Thickness without Liner (metric)
0.089 mm
Units per Case
9
Details
  • Double-coated
  • Aggressive, high-tack
  • Offers good heat resistance
  • White polyester film carrier with rubber adhesive on a kraft liner

3M™ Double Coated Tape 9816M is a 3.5-mil (0.09 mm), aggressive, high-tack, rubber-based adhesive that offers good heat resistance. It is intended for laminating open and closed cell foams where heat is not required. The tape adheres well to polyether, polyester urethane, polyethylene, polystyrene, vinyl foams and most rubbers.

Suggested Applications

  • Intended for laminating open and closed cell foams where heat is not required
  • Adheres well to polyether, polyester urethane, polyethylene, polystyrene, vinyl foams and most rubbers