- Maintains a strong bond under expansion, contraction, and limited movement
- Medium viscosity helps minimize running, dripping, or migration
- 25-minute work life with handling strength in approximately 150 minutes at room temperature
- Flows smoothly for controlled dispensing where needed
|
|
|
|---|---|
|
Adhesive Type
|
Epoxy
|
|
Applications
|
Encapsulating, Large Surface Lamination Assembly, Mounting & Trim Attachment, Panel to Frame/Stiffner to Panel Assembly, Potting, Sealing, Sealing, Potting and Encapsulating, Small Joint Assembly, Structural Bonding
|
|
Brand
|
Scotch-Weld™
|
|
Flame Retardant
|
UL94 HB
|
|
Full Cure Time
|
7 Days @ 72 F (22 C)
|
|
Hardness
|
55 Shore D
|
|
Indoor/Outdoor
|
Both
|
|
Industries
|
Construction, Consumer Goods, Electronics, General Industrial, Metalworking, Military and Government, Signage, Specialty Vehicle, Transportation, Woodworking
|
|
Maximum Operating Temperature (Fahrenheit)
|
300 °F
|
|
Mix Ratio Volume Base:Accelerator
|
1 : 1
|
|
Open Time
|
25 min @ 72 °F (22 °C)
|
|
Physical Form
|
Flowable Liquid
|
|
Position
|
Best
|
|
Product Colour
|
Transparent
|
|
Product Form
|
Cartridge
|
|
Product Type
|
Epoxy Adhesive
|
|
Set Time
|
10 min - 30 min
|
|
Shear Strength
|
2500 psi
|
|
Shelf Life in Months (from date of manufacture)
|
15
|
|
Specific Gravity
|
1.08, 1.15
|
|
Storage Temperature
|
60-80 F (16-27 C), 72 F (22 C)
|
|
Substrate
|
Ceramic, Elastomer, EPDM Rubber, Glass, Hardwood, High Surface Energy, (400-1100 Dynes/cm), LSE Plastic, Metal, Metal (Painted), Metal (Unpainted), Paint, Paint (Powder Coat, Painted Metal, Composite Panel), Plastic (ABS, PVC, Acrylic), Plastic (High Performance Nylon), Plastic (Polyolefins and Thermoplastic Elastomers), Plastic: HSE, MSE (ABS, Acrylic, Polycaronate, Nylon), Rubber (Except EPDM), Smooth, Stone, Vinyl Plasticized, Wood
|
|
Substrate 1
|
Glass, Metal, Paint, Plastic, Easy-to-Bond (HSE), Rubber (Except EPDM), Wood
|
|
Substrate 2
|
Ceramic, Elastomer, EPDM Rubber, Glass, Glass & Ceramics, High Surface Energy, (400-1100 Dynes/cm), LSE Plastic, Metal, Metal (Painted), Metal (Unpainted), Paint, Paint (Powder Coat, Painted Metal, Composite Panel), Plastic (ABS, PVC, Acrylic), Plastic (High Performance Nylon), Plastic (Polyolefins and Thermoplastic Elastomers), Plastic: HSE, MSE (ABS, Acrylic, Polycaronate, Nylon), Rubber (EPDM, Santoprene), Rubber (Except EPDM), Smooth, Stone, Vinyl Plasticized, Wood, Wood & Hardboard
|
|
Units per Case
|
12, 6
|
|
Viscosity
|
Self-leveling
|
|
Viscosity Range (cps) at Room Temperature
|
Base: 2,000-8,000, Accelerator: 22,000-33,000
|
|
Work Time
|
25 min
|
- Maintains a strong bond under expansion, contraction, and limited movement
- Medium viscosity helps minimize running, dripping, or migration
- 25-minute work life with handling strength in approximately 150 minutes at room temperature
- Flows smoothly for controlled dispensing where needed
- Flows smoothly for controlled dispensing where needed
The 3M™ Scotch-Weld Epoxy Adhesive DP125 is a low odour, two-part epoxy adhesive that creates strong structural and flexible bonds on metal, ceramics, wood, and many plastics. It provides the reliability and strength you need to maintain productive, cost-effective results.
The 3M™ Scotch-Weld™ Epoxy Adhesive DP125 is a versatile, medium viscosity epoxy adhesive that pours easily with minimal dripping, running, and migration that will flow smoothly for controlled, accurate dispensing. Its flexibility makes it ideal for applications involving dissimilar surfaces, where coefficients of thermal expansion are a consideration, for example when bonding glass to metals. The 1:1 mix ratio for our 3M™ Scotch-Weld™ Epoxy Adhesive DP125 is ideal with bulk mixing and with a 25-minute work life there's some opportunity for repositioning to keep projects on track. The adhesive reaches handling strength in approximately 150 minutes and is fully cured in 7 days (at 72°F/22°C).
Suggested Applications
- General attachment applications in a variety of industries
- Replace 5-minute epoxy for improved performance and more positioning time